sub0302_en

Characteristic

- Excellent electrical conductivity and mechanical properties
- Excellent heat dissipation characteristics
- Excellent injection properties

HIPS/MWCNT compound properties

Description	MWCNT amount used(wt %)	IZOD impact strength (1/4")	IZOD impact strength (1/8")	Melt FLow Rate	Hardenss	Heat Deflection Tempearature (1/4")	Tensile Strength	Tensile Elongation	Flexural Strength	Flexural Modules	Remarks
		kgf∙cm/cm	kgf∙cm/cm	g/10min	R-Scale	℃	kgf∙cm2	%	kgf∙cm2	kgf∙cm2
Virgin HIPS	0	9.00	13.00	6.00	99.00	82.00	270.00	62.00	430.00	21,700
MWCNT	2.55	6.80	7.93	0.92	93.80	80.80	290.30	31.70	440.70	21,333
ST3-MWCNT	2.55	4.50	7.40	0.32	96.10	81.60	312.30	22.00	476.30	22,770

PC/MWCNT compound properties

Description	MWCNT amount used(wt %)	IZOD impact strength (1/8")	Heat Deflection Temperature (1/4")	Tensile Strength	Tensile Elongation	Flexural Strength	Flexural Modules	Density (g/cm3)	Remarks
		kgf∙cm/cm	℃	kgf∙cm2	%	kgf∙cm2	kgf∙cm2
Virgin PC	0	76.5	126.0	673	120.0	979	24,575	1.200
MWCNT	2.55	14.6	126.5	628	15.00	981	24,746	-
ST1-MWCNT	2.55	13.8	127.3	664	18.00	1,055	25,833	-
ST1-MWCNT	4.76	21.6	122.0	672	-	1,192	-	1.232

Description	MWCNT amount used(wt %)	IZOD impact strength 1/4"	IZOD impact strength 1/8"	Melt Flow Rate	Heat Deflection Temperature 1/4"	Tensile Strength	Flexural Strength	Flexural Modules	Surface Resident	Remarks
		kgf∙cm/cm	kgf∙cm/cm	g/10min	℃	kgf∙cm2	kgf∙cm2	kgf∙cm2	Ω/☐
PP/MWCNT	3.85	4.28	9.7	1.53	116.3	256.4	375	15,292	>1E+12
PP/MWCNT	15	-	3044	-	-	309	432	-	>1E+2∼1E+3

PC/ABS/MWCNT properties

Sample name	NI (kgf∙cm/cm)		TS (kgf∙cm2)	ER (%)	FS (kgf∙cm2)	FM (kgf∙cm2)	Conductivity-Tensile specimens (log Ω/☐)			Conductivity- injection molding
	3.2mm	6.4mm>	50mm/min		3mm/min		gate	middle	terminal	log Ω/☐
natural PC/ABS	77.6	66.56	529.95	198.2	690	20957
	75.65	65.35
	79.82	61.36
	77.7	64.4	530.0	198.2	690	20957.0
PC/ABS NC7000 (3phr)	52.8	32.8	568.84	46.7	734	22231	12.15	13.2	9.26	High temperature
	49.89	33.15					13.15	12.54	8.15	4.94
	49.85	32.02					12.84	8.11	8.26	Low temperature
										4.65
	50.8	32.7	568.8	46.7	734.0	22231.0	12.71	11.28	8.56
PC/ABS DWC-NC7000 (3phr)	53.1	32.9	566.9	48.16	736	22471	9.04	9.34	8.48	High temperature
	52.33	34.01					9.26	8.15	8.2	3.98
	52.69	34.36					12.43	9.54	8.23	Low temperature
										3.95
	52.7	33.8	566.9	48.2	736.0	22471.0	10.24	9.01	8.30

PP/MWCNT compound properties

Description	MWCNT amount used(wt %)	IZOD impact strength 1/4"	IZOD impact strength 1/8"	Melt Flow Rate	Heat Deflection Temperature 1/4"	Tensile Strength	Flexural Strength	Flexural Modules	Surface Resident	Remarks
		kgf∙cm/cm	kgf∙cm/cm	g/10min	℃	kgf∙cm2	kgf∙cm2	kgf∙cm2	Ω/☐
PP/MWCNT	3.85	4.28	9.7	1.53	116.3	256.4	375	15,292	>1E+12
PP/MWCNT	15	-	3.44	-	-	309	432	-	1E+2∼1E+3

Nylon 6/MWCNT compound properties

Description	MWCNT amount used(wt %)	IZOD impact strength 1/8"	Melt Flow Rate	Heat Deflection Temperature 1/4"	Tensile Strength	Flexural Strength	Flexural Modules	Surface Resident	Remarks
		kgf∙cm/cm	g/10min	℃	kgf∙cm2	kgf∙cm2	kgf∙cm2	Ω/☐
Nylon 6/MWCNT	10	44	-	200	748.5	1,335.8	40,278.8	1E+4∼1E+5