Talc 컴파운드 물성
새로운 시대에 도전하며 여러분과 함께 나아가겠습니다.
HIPS/MWCNT 물성
| Description | Talc amount used(wt %) | Melt Flow Rate (g/10min) | Density (g/cm3) | Tensile Strength (MPa) | Tensile Elongation (%) | Flexural Strength (MPa) | Flexural Modules (MPa) | Izod impact strength 1/8" (23℃) | Heat Deflection Temperature 1/8"(℃) | Remarks |
|---|---|---|---|---|---|---|---|---|---|---|
| DWC-PP | 10 | 33.9 | 0.963 | 27 | 61 | 47.7 | 2,430 | 97 | 120 | |
| DWC-PP | 20 | 32.5 | 1.021 | 29.8 | 16 | 49.6 | 3,220 | 63 | 123 | |
| H Co. | 20 | ≧9 | 1.06±0.03 | ≧29 | ≧30 | ≧37 | ≧2.450 | ≧49 | ≧130 | |
| H Co. | 40 | ≧7 | 1.22±0.03 | ≧26 | ≧10 | ≧41 | ≧3.430 | ≧39 | ≧135 |
| Description | Talc amount used(wt %) | Flexural Modules (Kgf/cm2) | Flexural Strength (Kgf/cm2) | Tensile Strength (Kgf/cm2) | Tensile Elongation (%) | Heat Deflection Temperature (℃) | Izod impact strength (23℃) | Density (g/cm3) | Remarks |
|---|---|---|---|---|---|---|---|---|---|
| Nylon 6 | 0 | 28,000 | 1,100 | 780 | 30 | 65(18.6Kgf/cm2) | 6 | 1.13 | |
| DWC-Nylon 6 | 5 | 29,000 | 1,198 | 863 | 9.05 | 60.5(18.6Kgf/cm2) | 4.81 | 1.169 | |
| Nylon 6 | 15 | 37,000 | 1,100 | 750 | 6 | 95(18.6Kgf/cm2) | 4.0 | 1.23 | |
| Nylon 6 | 20 | 44,000 | 1,150 | 780 | 5 | 130(18.6Kgf/cm2) | 5 | 1.28 | |
| Nylon 6 | 30 | 55,000 | 1,250 | 800 | 4 | 160(18.6Kgf/cm2) | 5 | 1.36 |